The slow crack growth (SCG) parameters of soda-lime-silicate were measured in distilled and saltwater of various concentrations in order to determine if the presence of salt and the contaminate formation of a weak sodium film affects stress corrosion susceptibility. Past research indicates that solvents affect the rate of crack growth; however, the effects of salt have not been studied. The results indicate a small but statistically significant effect on the SCG parameters A and n at high concentrations; however, for typical engineering purposes, the effect can be ignored.

著录项

作者
Hausmann, B. D.; Salem, J. A.;
展开▼
作者单位

展开▼
年度 2016
页码 1-14
总页数 14
原文格式 PDF
正文语种 eng
中图分类工业技术;
关键词
Aqueous solutions; Crack propagation; Calcium oxides; Silica glass; Corrosion; Sodium chlorides; Stress intensity factors; Water; Fracture strength; Stresses; Data processing; Salinity; Minerals; Oceans;

机译：水溶液;裂纹扩展;氧化钙;硅玻璃;腐蚀;氯化钠;应力强度因子;水;断裂强度;应力;数据处理;盐度;矿物质;海洋;
入库时间 2022-08-29 10:46:11

相似文献

外文文献
中文文献
专利

1. Transgranular crack growth in the pipeline steels exposed to near-neutral pH soil aqueous solutions: Discontinuous crack growth mechanism [J] . Afolabi Egbewande, Weixing Chen, Reg Eadie, Corrosion science . 2014,第JUNa期

机译：暴露于接近中性pH值土壤水溶液的管线钢中的沿晶裂纹扩展：不连续裂纹扩展机制
2. Stochastic study on effects of material and physical parameters on slow crack growth behaviors of HDPE using the crack layer theory [J] . Wee Jung-Wook, Choi Byoung-Ho International Journal of Solids and Structures . 2020,第期

机译：用裂缝层理论对材料和物理参数对HDPE缓慢裂纹生长行为的影响的随机研究
3. Effects of recycled HDPE and nanoclay on stress cracking of HDPE by correlating J(c) with slow crack growth [J] . Na Sukjoon, Long Nguyen, Spatari Sabrina, Polymer engineering and science . 2018,第9期

机译：再生HDPE和纳米荧光对HDPE与缓慢裂纹生长的胁迫开裂的影响
4. EXPLORING THE EFFECTS OF LOW AMPLITUDE FATIGUE IN CRACK GROWTH RATES IN HIGH TEMPERATURE AQUEOUS SOLUTION/METAL SYSTEMS [C] . Mirna Urquidi-Macdonald, Digby D. Macdonald, Huai-Pu Chu CORROSION Annual Conference and Exposition . 1996

机译：探讨高温水溶液/金属系统裂纹生长速率低振幅疲劳的影响
5. Mechanistic modeling of corrosion fatigue crack growth of steels in aqueous solutions. [D] . Thomas, James Paul. 1989

机译：水溶液中钢的腐蚀疲劳裂纹扩展的力学模型。
6. Glass-to-cryogenic-liquid transitions in aqueous solutions suggested by crack healing [O] . Chae Un Kim, Mark W. Tate, Sol M. Gruner 2015

机译：裂纹修复表明水溶液中的玻璃到低温液体转变
7. The small fatigue crack growth behavior of an aluminum alloy in a sodium chloride aqueous solution. Stress amplitude and crack size dependence. [O] . Sotomi ISHIHARA, Kazyu MIYAO 1988

机译：氯化钠水溶液中铝合金的小疲劳裂纹生长行为。压力幅度和裂缝尺寸依赖性。

Effects of Aqueous Solutions on the Slow Crack Growth of Soda-Lime-Silicate Glass.

摘要

著录项

相似文献

相关主题

期刊订阅