首页> 美国政府科技报告 >Comparison of ceramic waste forms produced by hot uniaxial pressing and by cold pressing and sintering
【24h】

Comparison of ceramic waste forms produced by hot uniaxial pressing and by cold pressing and sintering

机译：通过热单轴压制和冷压和烧结产生的陶瓷废料形式的比较

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Synroc C waste form specimens prepared using the Australian-developed technology are uniaxially pressed in stainless steel bellows at 1200 deg C and 20MPa. This produces a material with high chemical and physical durability and with the radioactivity enclosed inside both the waste form and the bellows. An alternative method of producing the ceramic product is to use cold pressing of pellets followed by reactive sintering to provide densification and mineralization. Depending on the scale of waste form preparation required and on the activity level and nature of the waste streams, the cold press and sinter method may have advantages. To evaluate the effects of production method on waste form characteristics, especially resistance to dissolution or leaching of waste elements, we have prepared two simulated waste samples for evaluation. Both samples were prepared from liquid precursor materials (alkoxides, nitrates, and colloidal silica) and then doped with waste elements. The precursor material in each case corresponded to a basic phase assemblage of 60% zirconolite, 15% nepheline, 10% spinel, 10% perovskite, and 5% rutile. One sample was doped with 25% by weight of U; the other with 10% by weight each of U and Gd. Each sample was calcined at 750 deg C for 1 hr. in a 3.5% H2 in N2 atmosphere. Then one portion of each sample was hot pressed at temperatures ranging from 1120 to 1250 deg C and 20MPa pressure in steel bellows. A separate portion of each sample was formed into pellets, cold pressed, and sintered in various atmospheres at 1200 deg C to produce final products about 2/3 cm in diameter. Samples were then examined to determine density of the product, grain sizes of the phases, phase assemblage, and the location of the U and Gd in the final phases. Density data indicate that sintering gives good results provided that the samples are held at 200 deg C for long enough to allow trapped gases to escape.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号