首页> 美国政府科技报告 >Processing and Properties of Fiber Reinforced Polymeric Matrix Composites
【24h】

Processing and Properties of Fiber Reinforced Polymeric Matrix Composites

机译：纤维增强聚合物基复合材料的制备与性能

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The processability of a phenylethynyl terminated imide (PETI) resin matrixcomposite was investigated. Unidirectional prepregs were made by coating an N-methylpyrrolidone solution of the amide acid oligomer onto unsized IM7. Two batches of prepregs were used: one was made by NASA in-house, and the other was from an industrial source. The composite processing robustness was investigated with respect to the effect of B-staging conditions, the prepreg shelf life, and the optimal processing window. Rheological measurements indicated that PETI's processability was only slightly affected over a wide range of B-staging temperatures (from 250 C to 300 C). The open hole compression (OHC) strength values were statistically indistinguishable among specimens consolidated using various B-staging conditions. Prepreg rheology and OHC strengths were also found not to be affected by prolonged (i.e., up to 60 days) ambient storage. An optimal processing window was established using response surface methodology. It was found that IM7/PETI composite is more sensitive to the consolidation temperature than to the consolidation pressure. A good consolidation was achievable at 371 C/100 Psi, which yielded an OHC strength of 62 Ksi at room temperature. However, processability declined dramatically at temperatures below 350 C.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号