首页> 美国政府科技报告 >A comparison of graphite/epoxy tape laminates and 2-D braided composites mechanical properties
【24h】

A comparison of graphite/epoxy tape laminates and 2-D braided composites mechanical properties

机译：石墨/环氧树脂带层压板与二维编织复合材料力学性能的比较

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A comparison of the mechanical properties of unidirectional composite tape laminates and of two-dimensional triaxially braided composite was conducted. The tape laminate layups were designed to match the percentage of axial fibers and the angle of the bias tows in the braided composite. The materials system used for the laminates is AS4/3501-6 which was chosen as the closest available match to As4/1895 used for the braids. The strength and stiffness properties measured here include tension, open-hole tension, filled-hole tension, compression and open-hole compression, all of these in both the longitudinal and transverse direction. Results show that the longitudinal modulus of both material forms is quite similar, but that the transverse modulus of the braids is lower. In terms of strength, the longitudinal unnotched strength of the braids is lower than that of the laminates, while the transverse strength is significantly lower. For both strength and stiffness, the crimp in the bias tows of the braid is probably the main cause for reduced properties. On the other hand, a very significant increase in open-hole and filled-hole tension strength was observed for the braids compared to the tape laminates. However, this was not observed in compression where all the braid properties are lower than for the laminates.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号