首页> 美国政府科技报告 >(abstract) Undercooling Studies of the Bulk Metallic Glass Forming Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) Alloy During Containerless Electrostatic Levitation Processing
【24h】

(abstract) Undercooling Studies of the Bulk Metallic Glass Forming Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) Alloy During Containerless Electrostatic Levitation Processing

机译：（摘要）在无容器静电悬浮加工过程中形成Zr（sub 41.2）Ti（sub 13.8）Cu（sub 12.5）Ni（sub 10.0）Be（sub 22.5）合金的块状金属玻璃的过冷研究

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Bulk glass forming metallic alloys have long been desired for technological applications and for investigation into liquid undercooling, solidification processes, and thermophysical properties. A glass forming alloy Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) was used to investigate the thermal treatments affecting undercooling and vitrification. The experiments were performed using the high temperature high vacuum electrostatic levitator at JPL. A sample approximately 3 mm in diameter was melted, superheated, undercooled, and solidified while levitated in high vacuum. The results show that when the sample was held above its melting temperature for a sufficient period of time to dissolve oxides and then cooled faster than a critical cooling rate, it undercooled to the glass transition temperature, T(sub g), and formed a glassy alloy. The required critical cooling rate for metallic glass formation was obtained to be between 0.9 K per second and 1.2 K per second for the 42.4 mg sample.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号