首页> 美国政府科技报告 >Failure Mechanisms and Life Prediction of Thermal and Environmental Barrier Coatings under Thermal Gradients
【24h】

Failure Mechanisms and Life Prediction of Thermal and Environmental Barrier Coatings under Thermal Gradients

机译：热梯度下热和环境屏障涂层的失效机理和寿命预测

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Ceramic thermal and environmental barrier coatings (TEBCs) will play an increasingly important role in gas turbine engines because of their ability to further raise engine temperatures. However, the issue of coating durability is of major concern under high-heat-flux conditions. In particular, the accelerated coating delamination crack growth under the engine high heat-flux conditions is not well understood. In this paper, a laser heat flux technique is used to investigate the coating delamination crack propagation under realistic temperature-stress gradients and thermal cyclic conditions. The coating delamination mechanisms are investigated under various thermal loading conditions, and are correlated with coating dynamic fatigue, sintering and interfacial adhesion test results. A coating life prediction framework may be realized by examining the crack initiation and propagation driving forces for coating failure under high-heat-flux test conditions.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号