Controlling stress corrosion cracking in mechanism components of ground support equipment

机译：控制地面支护设备机构部件的应力腐蚀开裂

获取原文

页面导航

摘要
著录项
相似文献
相关主题

摘要

The selection of materials for mechanism components used in ground support equipment so that failures resulting from stress corrosion cracking will be prevented is described. A general criteria to be used in designing for resistance to stress corrosion cracking is also provided. Stress corrosion can be defined as combined action of sustained tensile stress and corrosion to cause premature failure of materials. Various aluminum, steels, nickel, titanium and copper alloys, and tempers and corrosive environment are evaluated for stress corrosion cracking.

著录项

作者
Majid, W. A.;
展开▼
作者单位

展开▼
年度 1988
页码 1-12
总页数 12
原文格式 PDF
正文语种 eng
中图分类工业技术;
关键词
CORROSION PREVENTION; CORROSION RESISTANCE; GROUND SUPPORT EQUIPMENT; STRESS CORROSION CRACKING; ALLOYS; FAILURE; FRACTURE STRENGTH; TENSILE STRESS;

机译：防腐;耐腐蚀性能;地面支持设备;应力腐蚀开裂;合金;失败;断裂强度;拉伸应力;

相似文献

外文文献
中文文献
专利

1. Crack Growth Characteristics of Aluminum Alloys Dominated by the Mechanisms of Fatigue and Stress Corrosion Cracking [J] . Ogawa Takeshi, Hasunuma Shota, Kato Shunsuke, Materials transactions . 2019,第11期

机译：抗疲劳和应力腐蚀机制主导的铝合金裂纹生长特性
2. Predicting the mechanisms and crack growth rates of pipelines undergoing stress corrosion cracking at high pH [J] . F.M. Song Corrosion science . 2009,第11期

机译：预测高pH应力腐蚀管道的机理和裂纹扩展率
3. NEW CONTRIBUTION TO MECHANISMS OF HYDROGEN-INDUCED CRACKING AND STRESS-CORROSION CRACKING [J] . 褚武扬自然科学进展：英文版 . 1991,第005期

机译：对氢气诱导的裂缝和腐蚀裂缝机制的新贡献
4. Mechanism-based Ageing Management of Primary Water Stress Corrosion Cracking of Ni-base Components in PWR Environments [C] . Tae Hyun Lee, Il Soon Hwang ICAPP 2008;International conference on advances in nuclear power plants . 2008

机译：压水堆环境中镍基成分一次水应力腐蚀开裂的基于机理的时效管理
5. Interfacial Degradation Mechanisms with Applications to Polymer-Matrix Composites and Intergranular Stress Corrosion Cracking of Steels [D] . Yavas, Denizhan. 2018

机译：界面降解机理及其在聚合物基复合材料中的应用和钢的晶间应力腐蚀开裂
6. Guard Cell Membrane Anion Transport Systems and Their Regulatory Components: An Elaborate Mechanism Controlling Stress-Induced Stomatal Closure [O] . Shunya Saito, Nobuyuki Uozumi 2019

机译：保卫细胞膜阴离子运输系统及其调控组件：控制压力诱导气孔闭合的精细机制
7. Microstructural and microchemical mechanisms controlling intergranular stress corrosion cracking in light-water-reactor systems [O] . Stephen M. Bruemmer, Gary S. Was 1994

机译：控制光 - 反应器系统中晶间应力腐蚀裂纹的微观结构和微型化学机制

Controlling stress corrosion cracking in mechanism components of ground support equipment

摘要

著录项

相似文献

相关主题

期刊订阅