首页> 美国政府科技报告 >Parameters Governing the Corrosion Protection Efficiency of Fusion-Bonded Epoxy Coatings on Reinforcing Steel
【24h】

Parameters Governing the Corrosion Protection Efficiency of Fusion-Bonded Epoxy Coatings on Reinforcing Steel

机译：熔融环氧树脂涂层对钢筋腐蚀防护效果的参数

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The purpose of this study was to investigate various epoxy coating and exposure parameters to determine their effects on the corrosion of reinforcing steel. The parameters investigated were: chloride content at the bar depth, coated bar corroded area, corrosion product color under the coating, epoxy coating adhesion, coating color, coating damage (holidays and holes), coating thickness, TGA, DSC and EDS analysis and SEM coating cracking investigation. This study demonstrated that the ECR coating samples extracted from concrete exhibited extensive cracking compared to the new ECR samples in which the coating cracking was limited to only one sample. The coating cracking correlated with the amount of chloride at bar level, residual adhesion of the epoxy to the steel surface, and the percent moisture in the coating. The coating cracking is also related to the change in color of the epoxy and indicates that the epoxy coating degradation in concrete influences the surface condition of the coating. The DSC results showed that both the extracted epoxy coating samples as well as new samples are not fully cured during the manufacturing process. Additionally, the extracted epoxy coated samples investigated presented significant permanent adhesion loss with little or no epoxy coating residue present on the bar surface, while the EDS analysis showed that once adhesion is lost, corrosion will proceed unimpeded under the coating even in the absence of chlorides.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号