首页> 外文OA文献 >Carbon Tetrachloride as a Thermoporometry Liquid Probe To Study the Cross-Linking of Styrene Copolymer Networks
【2h】

Carbon Tetrachloride as a Thermoporometry Liquid Probe To Study the Cross-Linking of Styrene Copolymer Networks

机译：四氯化碳作为热孔测量液探针，以研究苯乙烯共聚物网络的交联

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Mesh Size Distributions (MSDs) of swollen cross linked styrene copolymer networks have been measured by thermoporometry using CCl4 as a probe liquid. All numerical relationships required for the calculation of the MSD were established for both the liquid-to-solid and the solid-to-solid thermal transitions of CCl4 and successfully validated on test samples. It was found that the polymer network, for both thermally and photo-cross linked materials, was completely built in about four hours of exposure. A clear correlation was established between the average mesh size of the swollen polymer network on the one hand and the benzoyl peroxide groups content and swelling ratio on the other hand.
机译：通过使用CCl4作为探针液体，通过热压孔测量溶胀交联苯乙烯共聚物网络的网状尺寸分布（MSDS）。为CCL4的液体 - 固体和固体致热转变的液体和固体热转变而建立了计算MSD所需的所有数值关系，并在试验样品上成功验证。结果发现，对于热和光交联材料，聚合物网络完全建立在约4小时的曝光中。在一方面的溶胀聚合物网络的平均网格尺寸和苯甲酰基团的平均网格尺寸和另一方面，在苯甲酰基团含量和溶胀比之间建立了明显的相关性。