Friction and wear behaviour of dual phase steels in discontinuous sliding contact conditions as a function of sliding speed and contact frequency

机译：双相钢在不连续滑动接触条件下的摩擦磨损性能与滑动速度和接触频率的关系

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

© 2015 Elsevier Ltd. All rights reserved. Friction and wear rate behaviour of dual phase steel discs (DP600) as a function of sliding speed (0.05-3.75 m/s), and contact frequency (0.6-16.5 Hz) have been studied under unidirectional ball-on-disc dry sliding conditions. The coefficient of friction (COF) and wear rate exhibit not only a highly dependence on the sliding speed, but also on the contact frequency which appears to be the key factor determining the wear behaviour of the DP600 even at constant sliding speed. The wear mechanism is mainly oxidative. The validity of Garcia-Ramil-Celis model is demonstrated for discontinuous sliding contacts at contact frequencies below 7 Hz. However, above 7 Hz, the disc behaves as if it were subjected to a continuous sliding contact.
机译：©2015 Elsevier Ltd.保留所有权利。在单向球盘干式滑动条件下，研究了双相钢盘（DP600）的摩擦磨损率行为与滑动速度（0.05-3.75 m / s）和接触频率（0.6-16.5 Hz）的关系。摩擦系数（COF）和磨损率不仅高度依赖于滑动速度，而且还依赖于接触频率，即使在恒定的滑动速度下，接触频率也是决定DP600磨损行为的关键因素。磨损机理主要是氧化性的。证明了Garcia-Ramil-Celis模型对于接触频率低于7 Hz的不连续滑动接触的有效性。但是，高于7 Hz时，光盘的行为就像是受到连续的滑动接触。