首页> 外文OA文献 >Oxide coarsening and its influence on recrystallization in a mechanically alloyed Fe-base oxide-dispersion-strengthened alloy
【2h】

Oxide coarsening and its influence on recrystallization in a mechanically alloyed Fe-base oxide-dispersion-strengthened alloy

机译：机械合金化铁基氧化物弥散强化合金中的氧化物粗化及其对再结晶的影响

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Analytical transmission electron microscopy has been used to determine whether yttria particles readily coarsen in oxide-dispersion-strengthened ferritic stainless alloy (PM2000), in an attempt to contribute to a model that explains the directionality of the microstructure observed when this material undergoes recrystallization under isothermal conditions. Likewise, the role of Al2O3 particles in the recrystallization processes of alumina-enriched PM2000 alloy has been studied via the addition of 1 wt pct Al2O3 particles as dispersoids. A carbon extraction replica technique was used to show that no coarsening of the yttria dispersion occurred even under exaggerated heat treatment at 1380 °C for 1 hour. By contrast, a significant ripening of alumina particles occurred apparently without influence on the recrystallization processes.
机译：分析型透射电子显微镜已用于确定氧化钇强化的铁素体不锈钢合金（PM2000）中的氧化钇颗粒是否易于粗大化，以试图为解释该材料在等温下进行重结晶时观察到的微观结构的方向性做出贡献的模型。条件。同样，通过添加1 wt％的Al2O3颗粒作为弥散体，研究了Al2O3颗粒在富铝PM2000合金重结晶过程中的作用。使用碳提取复制技术显示即使在1380°C进行1小时的夸大热处理，氧化钇分散体也不会粗化。相比之下，氧化铝颗粒明显发生了明显的熟化，而不影响重结晶过程。

著录项

  • 作者

    Capdevila, Carlos;

  • 作者单位
  • 年度 2013
  • 总页数
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类

相似文献

  • 外文文献
  • 中文文献
  • 专利
代理获取

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号