首页> 外文OA文献 >Layer growth mechanisms on metallic electrodes under anodic polarization in cryolite-alumina melt
【2h】

Layer growth mechanisms on metallic electrodes under anodic polarization in cryolite-alumina melt

机译:冰晶石-氧化铝熔体中阳极极化下金属电极上的层生长机理

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务,本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文,但由于OA文献来源多样且变更频繁,仍可能出现获取不到、文献不完整或与标题不符等情况,如果获取不到我们将提供退款服务。请知悉。

摘要

The anodic behavior of Fe, Ni, Co electrodes was investigated in a cryolite-alumina melt at 960 °C, by electrochemical techniques, microstructural characterizations and thermodynamic calculations, to provide a fundamental understanding of layers formation at metal (M) electrode surface. At low overpotential, anodic dissolution of M occurs; when the Mn+ concentration at the surface reaches saturation, a MxAl3-xO4 spinel phase precipitates. Then, a dense MyO layer grows at the metal/spinel interface. As for Fe, polarization at higher overpotentials lead to the same layers of spinel and monoxide, but pores at the metal/FeyO interface cause loss of adhesion of the oxide film.
机译:Fe,Ni,Co电极在960°C的冰晶石-氧化铝熔体中的阳极行为通过电化学技术,微观结构表征和热力学计算进行了研究,以提供对金属(M)电极表面形成层的基本了解。在低超电势下,M发生阳极溶解。当表面的Mn +浓度达到饱和时,会析出MxAl3-xO4尖晶石相。然后,致密的MyO层在金属/尖晶石界面生长。对于Fe,在较高的超电势下极化会导致形成相同的尖晶石和一氧化碳层,但是金属/ FeyO界面的孔会导致氧化膜的粘附性降低。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
代理获取

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号