首页> 外文OA文献 >Rotational Resonance Vibrometry on Ceramic Components
【2h】

Rotational Resonance Vibrometry on Ceramic Components

机译：陶瓷组件上的旋转共振振动法

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Let us assume an isotropic solid with rotational symmetry. If a pulse is injected normal to the surface, this excitation will result in a vibration along the same direction. This is true for any point around the circumference: The rotational symmetry of geometry and material results in a „rotational symmetry“ of the response. If the sample is rotated by an arbitrary angle between two measurements, one finds always the same result. As a consequence, reduction of symmetry (e.g. presence of defect, anisotropy of material, non-rotational geometry) causes an anisotropic response: In most cases the response is a superposition of two oszillations: A resonance split (Fig. 1b).
机译：让我们假设具有旋转对称性的各向同性固体。如果垂直于表面注入脉冲，则该激励将导致沿相同方向的振动。对于圆周上的任何点都是如此：几何形状和材料的旋转对称导致响应的“旋转对称”。如果在两次测量之间将样品旋转任意角度，则总是会发现相同的结果。结果，对称性的降低（例如缺陷的存在，材料的各向异性，非旋转的几何形状）会引起各向异性响应：在大多数情况下，响应是两个振动的叠加：共振分裂（图1b）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
代理获取

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号