The feasibility of the defect detection in friction stir welds of aluminum alloys with the use of two different non-destructive testing (NDT) methods has been studied. We have used the following NDT techniques: ultrasonic phase array and eddy current methods. A metallographic examination was chosen as the third method. The weld flaws such as kissing bond boundaries, lack of penetration, voids and cracks have been successfully detected using the ultrasonic phase array technique. The eddy current method enabled the detection of a weld root flaw.
机译：研究了使用两种不同的无损检测（NDT）方法检测铝合金摩擦搅拌焊缝中缺陷的可行性。我们使用了以下NDT技术：超声相控阵和涡流方法。金相检验被选为第三种方法。使用超声波相控阵技术已成功检测到焊接缺陷，例如接吻结合边界，缺乏熔深，空隙和裂纹。涡流法能够检测焊缝根部缺陷。