首页> 外文OA文献 >Effects of damage rate on Cu precipitation in Fe–Cu model alloys under neutron irradiation
【2h】

Effects of damage rate on Cu precipitation in Fe–Cu model alloys under neutron irradiation

机译：损伤率对中子辐照下Fe–Cu模型合金中Cu析出的影响

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The formation of Cu precipitates and point defect clusters was investigated in two Fe–Cu binary model alloys, Fe–0.3Cu and Fe–0.6Cu, irradiated at 573 K at three different damage rates, namely 3.8 × 10[−10], 1.5 × 10[−8] and 5 × 10[−8] dpa (displacements per atom)/s, up to about 1.6 × 10[−2] dpa. Results of positron annihilation experiments indicated that Cu precipitates were formed in these irradiations with different damage rates. The growth of Cu precipitates does not increase monotonously with increasing irradiation dose, but it rather depends on the nucleation and growth of microvoids. It is also clear that the nucleation and growth of microvoids are influenced by the irradiation dose rate.
机译：研究了两种Fe–Cu二元模型合金Fe–0.3Cu和Fe–0.6Cu在573 K照射下三种不同的损伤率，即3.8×10 [−10]，1.5对Cu沉淀的形成和点缺陷簇的形成。 ××10 [-8]和5××10 [-8] 8dpa（每原子的位移）/ s，直至约1.6××10 [-2] dpa。正电子an没实验的结果表明，在这些辐照下形成了具有不同损伤率的Cu沉淀。 Cu沉淀物的生长不会随辐照剂量的增加而单调增加，而是取决于微孔的成核和生长。同样清楚的是，微孔的成核和生长受辐射剂量率的影响。

著录项

  • 作者

    Xu Q.; Yoshiie T.;

  • 作者单位
  • 年度 2011
  • 总页数
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类

相似文献

  • 外文文献
  • 中文文献
  • 专利
代理获取

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号