首页> 外文OA文献 >Persistence of superconducting condensate far above the critical temperature in YBa$_2$(Cu,Zn)$_3$O$_y$ revealed by $c$-axis optical conductivity measurements for several Zn concentrations and carrier doping levels
【2h】

Persistence of superconducting condensate far above the critical temperature in YBa$_2$(Cu,Zn)$_3$O$_y$ revealed by $c$-axis optical conductivity measurements for several Zn concentrations and carrier doping levels

机译：超导冷凝物的持久性远高于临界值   温度在YBa $ _2 $（铜，锌）$ _ 3 $ O $ _y $由$ c $ -axis optical透露   几种Zn浓度和载流子掺杂的电导率测量   水平

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The superconductivity precursor phenomena in high temperature cupratesuperconductors was studied by direct measurements of superconductingcondensate with the use of the $c$-axis optical conductivity ofYBa$_{2}$(Cu$_{1-x}$Zn$_{x}$)$_{3}$O$_{y}$ for several doping levels ($p$) aswell as for several Zn-concentrations. Both of the real and imaginary part ofthe optical conductivity clearly showed that the superconducting carrierspersist up to the high temperatures $T$$_{p}$ that is higher than the criticaltemperature $T$$_{c}$ but lower than the pseudogap temperature $T$$^{\ast}$.$T$$_{p}$ increases with reducing doping level like $T$$^{\ast}$, but decreaseswith Zn-substitution unlike $T$$^{\ast}$.
机译：通过使用YBa $ _ {2} $（Cu $ _ {1-x} $ Zn $ _ {x}的$ c $轴光导率直接测量超导冷凝物，研究了高温铜酸盐超导体中的超导前体现象。 $）$ _ {3} $ O $ _ {y} $用于几种掺杂水平（$ p $）以及几种Zn浓度。光学导率的实部和虚部都清楚地表明，超导载流子一直保持到高于临界温度$ T $$ _ {c} $的高温$ T $$ _ {p} $，但低于伪间隙温度$ T $$ ^ {\ ast} $。$ T $$ _ {{}} $会随着掺杂水平的降低而增加，例如$ T $$ ^ {\ ast} $，但是与$ T $$ ^ { \ ast} $。