首页> 外文OA文献 >Anisotropy of the acoustooptic figure of merit for LiNbO3 crystals. Isotropic diffraction
【2h】

Anisotropy of the acoustooptic figure of merit for LiNbO3 crystals. Isotropic diffraction

机译：LiNbO3晶体的声光品质因数的各向异性。   各向同性衍射

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We have developed the approach for analyzing of anisotropy of acoustoopticfigure of merit (AOFM) for lithium niobate crystals in the case of isotropicacoustooptic (AO) diffraction. The working relations for the effectiveelastooptic coefficients and the AOFM have been derived. We have found that,under the conditions of isotropic AO diffraction, the maximum AOFM value forLiNbO3 is equal tp 11.62x10-15s3/kg. It is peculiar for the geometry of AOinteraction of the shear acoustic wave propagating in the YZ plane (thevelocity 3994 m/s) with the optical wave polarized in the same plane. We havedemonstrated that the maximum AOFM values are achieved mainly due to essentialanisotropy and high values of the elastooptic coefficients of LiNbO3.
机译：我们已经开发了在各向同性声光（AO）衍射情况下分析铌酸锂晶体的声品质因数各向异性（AOFM）的方法。推导了有效弹性系数和AOFM的工作关系。我们已经发现，在各向同性AO衍射条件下，LiNbO3的最大AOFM值等于tp 11.62x10-15s3 / kg。对于在YZ平面（速度3994 m / s）中传播且光波在同一平面中偏振的剪切声波的AO相互作用的几何形状而言，这是特有的。我们已经证明达到最大AOFM值的主要原因是本质各向异性和LiNbO3的弹性系数高。