TiAl TiAl TiAl-BASED ALLOY HAVING EXCELLENT HIGH-TEMPERATURE FORMABILITY AND METHOD FOR MANUFACTURING TiAl-BASED ALLOY MEMBER USING THE SAME
TiAl TiAl TiAl-BASED ALLOY HAVING EXCELLENT HIGH-TEMPERATURE FORMABILITY AND METHOD FOR MANUFACTURING TiAl-BASED ALLOY MEMBER USING THE SAME
展开▼
机译:具有卓越的高温成形性的TiAl TiAl基TiAl基合金及其制造TiAl基合金部件的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention, (a) 40.0 to 42.0 atomic% aluminum (Al); 5.0 to 7.0 atomic% niobium (Nb); 3.0 to 5.0 atomic percent vanadium (V); 1.0 to 3.0 atomic% iron (Fe); 0.2 to 0.4 atomic% silicon (Si); 0.1 to 0.3 atomic% of boron (B); Carbon (C) greater than 0 atomic% and up to 0.2 atomic%; Titanium (Ti) balance; And TiAl-based alloy having excellent high-temperature formability including inevitable impurities and a method of manufacturing a TiAl-based alloy member using the same, the novel TiAl-based alloy according to the present invention has significantly improved high-temperature molding compared to the existing TiAl-based alloy It can greatly reduce the manufacturing process of TiAl-based alloy members such as high-temperature engine parts and significantly reduce manufacturing costs. In addition, according to the method of manufacturing a member using the TiAl-based alloy according to the present invention, the TiAl with improved fracture toughness and creep resistance is improved by performing an optimized heat treatment after easily performing a molding process using the TiAl-based alloy having excellent high-temperature formability Based alloy member can be produced.
展开▼