HOT-ROLLED Nb-CONTAINING FERRITIC STAINLESS STEEL SHEET AND METHOD FOR PRODUCING SAME, AND COLD-ROLLED Nb-CONTAINING FERRITIC STAINLESS STEEL SHEET AND METHOD FOR PRODUCING SAME

机译：热轧含铌铁素体不锈钢薄板及其制造方法，冷轧含铌铁素体不锈钢薄板及其制造方法

页面导航

摘要
著录项
相似文献

摘要

The hot-rolled Nb-containing ferritic stainless steel sheet of the present invention has a composition containing C: 0.030 mass % or less, Si: 2.00 mass % or less, Mn: 2.00 mass % or less, P: 0.050 mass % or less, S: 0.040 mass % or less, Cr: 10.00 mass % to 25.00 mass %, N: 0.030 mass % or less and Nb: 0.01 mass % to 0.80 mass %, with the balance being made up of Fe and unavoidable impurities. In this hot-rolled Nb-containing ferritic stainless steel sheet, the precipitation amount of Nb carbonitrides is 0.2 mass % or more, and the number of Laves phases having a grain size of 0.1 μm or less is 10 or fewer per 10 μm²of surface area.

机译：本发明的热轧含Nb铁素体系不锈钢板的组成为：C：0.030质量％以下，Si：2.00质量％以下，Mn：2.00质量％以下，P：0.050质量％以下S，S：0.040质量％以下，Cr：10.00质量％〜25.00质量％，N：0.030质量％以下，Nb：0.01质量％〜0.80质量％，余量由Fe和不可避免的杂质构成。在该热轧含Nb铁素体系不锈钢板中，Nb碳氮化物的析出量为0.2质量％以上，晶粒尺寸为0.1μm以下的Laves相的数量为每10μm≤10。 > 2 的表面积。

著录项

公开/公告号US2020255919A1

专利类型
公开/公告日2020-08-13

原文格式PDF
申请/专利权人 NIPPON STEEL STAINLESS STEEL CORPORATION;
展开▼

申请/专利号US202016845327
发明设计人 YUTAKA YAKUSHIJIN;AKIRA HIRONAKA;KAZUNARI IMAKAWA;
展开▼

申请日2020-04-10
分类号C21D9/46;C22C38/50;C22C38/48;C22C38/44;C22C38/42;C22C38/06;C22C38/02;C22C38;C21D8/02;C21D6;B21B3/02;C21D9/48;C21D8/04;C22C38/58;C22C38/38;