STEEL FOR STEEL FORGING AND FORGED STEEL CRANK THROW AND FORGED STEEL JOURNAL FOR ASSEMBLING TYPE CRANKSHAFT
STEEL FOR STEEL FORGING AND FORGED STEEL CRANK THROW AND FORGED STEEL JOURNAL FOR ASSEMBLING TYPE CRANKSHAFT
展开▼
机译:锻造用钢和锻造用钢的曲柄抛掷和锻造用钢装配式曲轴的杂志
展开▼
页面导航
摘要
著录项
相似文献
摘要
The steel for forgings according to the present invention is characterized in that the steel contains, by mass%, C: 0.28% to 0.47%, Si: 0% to 0.45%, Mn: 0.90 to 1.50% More than 0% to 0.30% or less, Mo: more than 0% to 0.15% or less, and V: 0.06% or more to 0.32% or less and the remainder being iron and inevitable impurities, is a total area ratio of not less than 90%, the equivalent circle diameter and the number density of at least 55 / μm 2 500 gae / μm 2 or less of the pro-eutectoid ferrite of V-carbides than 50nm, yield stress of at least 420MPa, fatigue The strength is more than 330 MPa. Thus, excellent workability, high yield stress and high fatigue strength can be realized.