High strength Cu—Ni—Co—Si based copper alloy sheet material and method for producing the same, and current carrying component
High strength Cu—Ni—Co—Si based copper alloy sheet material and method for producing the same, and current carrying component
展开▼
机译：高强度Cu-Ni-Co-Si基铜合金板材及其制造方法和载流元件
展开▼
页面导航
摘要
著录项
相似文献
摘要
A copper alloy sheet material comprises (by mass %) from 2.50 to 4.00% in total of Ni and Co, from 0.50 to 2.00% of Co, from 0.70 to 1.50% of Si, from 0 to 0.50% of Fe, from 0 to 0.10% of Mg, from 0 to 0.50% of Sn, from 0 to 0.15% of Zn, from 0 to 0.07% of B, from 0 to 0.10% of P, from 0 to 0.10% of REM, from 0 to 0.01% in total of Cr, Zr, Hf, Nb and S, the balance Cu and unavoidable impurities. A number density of coarse secondary phase particles (particle diameter of 5 mm or more) is 10 per mm2 or less. A number density of fine secondary phase particles (particle diameter of from 5 to 10 nm) is 1.0·109 per mm2 or more. A Si concentration in the parent phase is 0.10% by mass or more.