ALUMINIUM ALLOY EXTRUDED MATERIAL WITH EXCELLENT MACHINABILITY AND MANUFACTURING METHOD THEREOF
ALUMINIUM ALLOY EXTRUDED MATERIAL WITH EXCELLENT MACHINABILITY AND MANUFACTURING METHOD THEREOF
展开▼
机译:具有优异可加工性的铝合金挤压材料及其制造方法
展开▼
页面导航
摘要
著录项
摘要
To obtain an Al-Mg-Si based aluminum alloy extruded material with a smooth surface and no burning without inhibiting the productivity. An aluminum alloy billet includes: Si: 2.0 to 6.0% by mass; Mg: 0.3 to 1.2% by mass; and Ti: 0.01 to 0.2% by mass, a Fe content being restricted to 0.2% or less by mass, with the balance being Al and inevitable impurities. The aluminum alloy billet is subjected to a homogenization treatment by keeping at 500 to 550°C for 4 to 15 hours. The billet is forcibly cooled to 250°C or lower at an average cooling rate of 50°C/hr or higher. Then, the billet is subjected to hot-extruding at an extrusion rate of 3 to 10 m/min by being heating at 450 to 500°C. The extruded material is forcibly cooled at an average cooling rate of 50°C/sec or higher and then subjected to an aging treatment. The extruded material can be manufactured that has its surface having a ten-point average roughness Rz of 80 µm or less.
展开▼