ALUMINUM BASED AL3ZR ALLOY COMPOSITION FOR OVERHEAD CONDUCTOR WIRE ROD
ALUMINUM BASED AL3ZR ALLOY COMPOSITION FOR OVERHEAD CONDUCTOR WIRE ROD
展开▼
机译:架空导线的基于铝的Al3Zr合金成分
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present disclosure provides an aluminum based Al3Zr alloy composition for manufacturing an aluminum alloy conductor. The aluminum based Al3Zr alloy composition includes 99.25 to 99.5 % aluminum by weight. In addition, the aluminum based Al3Zr alloy composition includes 0.001 to 0.002 % boron by weight, 0.010 to 0.050 % copper by weight and 0.200 to 0.350 % zirconium by weight. Moreover, the aluminum based alloy Al3Zr composition includes 0.050 to 0.070 % silicon by weight and 0.150 to 0.190 % iron by weight. Moreover, the aluminum alloy conductor wire rod has a pre-defined ultimate tensile strength in a range of 150 MPa to 200 MPa. TO BE PUBLISHED WITH FIGURE-1