Steel for induction hardening, roughly shaped material for induction hardening, producing method thereof, and induction hardening steel part

机译：感应淬火用钢，感应淬火用的异型材，其制造方法以及感应淬火用钢零件

页面导航

摘要
著录项
相似文献

摘要

A steel for an induction hardening including, by mass %, C: more than 0.75% to 1.20%, Si: 0.002 to 3.00%, Mn: 0.20 to 2.00%, S: 0.002 to 0.100%, Al: more than 0.050% to 3.00%, P: limited to 0.050% or less, N: limited to 0.0200% or less, O: limited to: 0.0030% or less, and the balance composing of iron and unavoidable impurities, wherein an Al content and a N content satisfy, by mass %, Al−(27/14)×N0.050%.

机译：用于感应淬火的钢，以质量％计，C：大于0.75％至1.20％，Si：0.002至3.00％，Mn：0.20至2.00％，S：0.002至0.100％，Al：大于0.050％ 3.00％，P：限制为0.050％以下，N：限制为0.0200％以下，O：限制为：0.0030％以下，并且由Al和N含量满足的余量由铁和不可避免的杂质组成，按质量％计，Al-（27/14）×N＞ 0.050％。

著录项

公开/公告号US9039962B2

专利类型
公开/公告日2015-05-26

原文格式PDF
申请/专利权人 MANABU KUBOTA;TOSHIHARU AISO;KEI MIYANISHI;
展开▼

申请/专利号US201113637414
发明设计人 MANABU KUBOTA;TOSHIHARU AISO;KEI MIYANISHI;
展开▼

申请日2011-02-15
分类号C22C38/08;C21D9/32;C21D1/18;C21D1/42;C21D9/30;C21D9/40;C22C38;C22C38/02;C22C38/04;C22C38/06;C22C38/18;C22C38/60;C22C38/12;C22C38/14;C22C38/16;C22C38/20;C22C38/22;C22C38/24;C22C38/26;C22C38/28;
国家 US
入库时间 2022-08-21 15:19:43

相似文献

专利
外文文献
中文文献