首页> 外国专利> Mold flux for casting TWIP with high Al content and method for producing TWIP using the same

Mold flux for casting TWIP with high Al content and method for producing TWIP using the same

机译：用于铸造高Al含量的TWIP的保护渣及使用该保护渣的制造TWIP的方法

页面导航

摘要
著录项
相似文献

摘要

The invention and Al-containing TWIP steel casting mold fluxes and relates to TWIP steel producing method using the same , SiO ₂ 36 to 38 wt %, CaO 25 to 28 wt %, MgO 2.5 to 3.5 wt %, Al ₂ O ₃ 6 to 7 parts by weight , Na ₂ O 14.5 to 15.5 wt %, F 9.5 to 10.5 wt %, Li ₂ O 2.5 to 3.5 % by weight of the mold flux that contains the service and , Furthermore , the mold flux , and melting the composition of the above-described steps; And were introduced into the melt of the mold flux to the mold and provides a method of producing ultra-high strength steel plate (TWIP) comprises the step of casting . ;

机译：本发明涉及一种含铝的TWIP钢铸模助熔剂，涉及使用该TWIP钢铸模助熔剂的SiO _{2 36-38 wt％，CaO 25-28 wt％，MgO 2.5-3.5 wt％，Al _{2 O _{3 6至7重量份，Na _{2 O 14.5至15.5 wt％，F 9.5至10.5 wt％，Li _{2 O含有助焊剂的铸模助焊剂的2.5-3.5重量％，此外，还包括铸模助熔剂和上述步骤的熔融组成;并被引入到熔模中的熔剂到模具中，并提供了一种生产超高强度钢板的方法（TWIP），包括铸造步骤。 ;}}}}}

著录项

公开/公告号KR101371959B1

专利类型
公开/公告日2014-03-10

原文格式PDF
申请/专利权人
展开▼

申请/专利号KR20110118795
发明设计人 박민석;
展开▼

申请日2011-11-15
分类号B22D11/108;B22D11/07;
国家 KR
入库时间 2022-08-21 15:41:23