Copper alloy having high strength and superior bending workability, and method for manufacturing copper alloy plates
Copper alloy having high strength and superior bending workability, and method for manufacturing copper alloy plates
展开▼
机译:具有高强度和优异弯曲加工性的铜合金及其制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to copper alloys to have high-intensitive and excellent bendability, separately includes 0.01 to 3.0% mass parts, 0.01 to 0.4% piece of P of Fe and 0.1 to 1.0% mass M g, remaining is Cu and inevitable impurity, whereinIn grain diameter measurement by crystal orientation analysis method, wherein electron backscattered modular system is mounted on field emission scanning electron microscope, average grain diameter describes 6.5 m or less, the standard deviation partial size with mean as described below are 1.5 m or smaller: wherein when n indicates to indicate measured value in the grain diameter measurement and x of crystal grain, average grain diameter is (Σ x)/n, and the standard deviation partial size with mean is [n Σ x2-dichloro (/) 2] Σ x [n/ (n-1) 1/2].
展开▼
机译:本发明涉及具有高强度和优异弯曲性的铜合金,分别包括0.01至3.0%质量份,0.01至0.4%的Fe铁和0.1至1.0%质量的M g,剩余的是Cu和不可避免的杂质,其中在通过晶体取向分析方法进行的粒径测量中,其中将电子背散射模块系统安装在场发射扫描电子显微镜上,平均粒径描述为6.5 m或更小,标准偏差部分尺寸的平均值如下所述为1.5 m或更小:其中当n表示晶粒直径测量中的测量值和晶粒的x时,平均晶粒直径为(Σx)/ n,平均值的标准偏差部分尺寸为[nΣx2-二氯(/)2]Σ x [n /(n-1)1/2]。
展开▼