LIFE ESTIMATION OF METALLIC MATERIAL DUE TO OCCURRENCE OF STRESS CORROSION CRACK, AND INSPECTION PLANNING SYSTEM FOR STRUCTURE USED UNDER CORROSIVE WATER ENVIRONMENT
LIFE ESTIMATION OF METALLIC MATERIAL DUE TO OCCURRENCE OF STRESS CORROSION CRACK, AND INSPECTION PLANNING SYSTEM FOR STRUCTURE USED UNDER CORROSIVE WATER ENVIRONMENT
展开▼
机译:应力腐蚀引起金属材料的寿命估算以及在腐蚀性水环境下使用的结构检查计划系统
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a method for quantitatively estimating life until the occurrence of a stress corrosion crack (SCC) in a metallic material to constitute a structure used under corrosive environment.SOLUTION: A metallic material exhibits susceptibility to the occurrence of SCC at a configured lower limit px of the thickness of a surface oxide film. The time tx for the thickness p of the surface oxide film to reach the lower limit px is obtained from the time dependency of the surface oxide film shown as a solid line in a drawing. Subsequently, an event as a fracture factor of the surface oxide film is assumed. In the case that the event occurs after the reaching time tx, the occurrence of SCC is possible due to the corrosion progress in a base material resulting from the breaking of the oxide film. An SCC progress due to the corrosion of base material is shown as a dash line in a drawing. The possibility whether the occurrence of SCC is present or not is then determined. When the resulting determination is that the possibility of the occurrence of SCC is present, the event occurrence time is estimated as life L until the occurrence of SCC.
展开▼