CORROSION RESISTANT NICKEL ALLOY COMPOSITIONS WITH ENHANCED CASTABILITY AND MECHANICAL PROPERTIES
CORROSION RESISTANT NICKEL ALLOY COMPOSITIONS WITH ENHANCED CASTABILITY AND MECHANICAL PROPERTIES
展开▼
机译:具有增强的稳定性和机械性能的耐腐蚀镍合金成分
展开▼
页面导航
摘要
著录项
相似文献
摘要
Disclosed are novel nickel-base alloy compositions that may be cast as a single crystal or directionally solidified alloy consisting of, by weight: 8-12% Cr, 10-14% Co, 0.3-0.9% Mo, 3-7% W, 2-8% Ta, 2.0-5.5% Al, 1.5-5.0 % Ti, up to 2% Nb, less than 0.1% B, less than 0.1% Zr, 0.05-0.15% C, less than 0.5% Hf, 2-4% Re, 0.05-0.2% Si, up to 0.015% S, up to 0.1% La, up to 0.1% Y, up to 0.1% Ce, up to 0.1% Nd, up to 0.1% Dy, up to 0.1% Pr, up to 0.1% Gd, balance Ni, and wherein (La+Y+Ce+Nd+Dy+Pr+Gd) is 0.001-0.1%. The compositions for the nickel-base superalloy have a balance between oxidation resistance, corrosion resistance, castability, and mechanical properties, such as creep resistance and thermo-mechanical fatigue resistance.
展开▼
机译:公开了新颖的镍基合金组合物,其可以铸造为单晶或定向凝固的合金,其按重量计包括:8-12%Cr,10-14%Co,0.3-0.9%Mo,3-7%W, 2-8%Ta,2.0-5.5%Al,1.5-5.0%Ti,高达2%Nb,小于0.1%B,小于0.1%Zr,0.05-0.15%C,小于0.5%Hf,2- 4%Re,0.05-0.2%Si,最高0.015%S,最高0.1%La,最高0.1%Y,最高0.1%Ce,最高0.1%Nd,最高0.1%Dy,最高0.1% Pr,最高为0.1%Gd,其余为Ni,并且其中(La + Y + Ce + Nd + Dy + Pr + Gd)为0.001-0.1%。用于镍基高温合金的组合物在耐氧化性,耐腐蚀性,可铸造性和机械性能如耐蠕变性和耐热机械疲劳性之间达到平衡。
展开▼