CARBURIZED AND QUENCHED STEEL EXCELLENT IN LOW CYCLE FATIGUE PROPERTY, AND CARBURIZED AND QUENCHED COMPONENT
CARBURIZED AND QUENCHED STEEL EXCELLENT IN LOW CYCLE FATIGUE PROPERTY, AND CARBURIZED AND QUENCHED COMPONENT
展开▼
机译:低循环疲劳性能的渗碳和淬火钢,以及渗碳和淬火的成分
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a carburized and quenched steel excellent in low cycle fatigue properties.;SOLUTION: The carburized and quenched steel is characterized in that the hardness at a position of 13 mm from the quenched edge in a Jominy test is ≥60×C0.5-5(HRC); and A=(Mo+0.227Ni+190B-0.087Si-17.2P-2.74V-7.18Cs-0.00955Hs+0.0344Nγ) and B=(t×(Hcore)2) satisfy the relation of A-0.00000293×B≥14; wherein, Hcore is a core hardness; (t) is an effective hardened layer depth; (r) is the radius of the failure zone of the half of the wall thickness of the failure zone; Cs is the carburization concentration (mass%) in the surface layer; Hs is a surface hardness (Hv); and Nγis the old austenite grain size of a carburized layer.;COPYRIGHT: (C)2011,JPO&INPIT
展开▼