TIG WELDING METHOD TO IMPROVE PITTING CORROSION RESISTANCE OF 22Cr DUPLEX STAINLESS STEEL WELDS
TIG WELDING METHOD TO IMPROVE PITTING CORROSION RESISTANCE OF 22Cr DUPLEX STAINLESS STEEL WELDS
展开▼
机译:TIG焊接方法以提高22%Cr双相不锈钢焊缝的抗点蚀性能
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: A TIG welding method is provided to improve pitting resistance of a welding part by uniformly distributing an austenite-phase and a ferrite-phase while preventing denitrification. CONSTITUTION: A TIG welding method is carried out with respect to a two-phase stainless steel including Cr 20-30%, Ni 4-10%, Mo 1.5-5.0%, N 0.1-0.5%, C 0.01-0.05%, Fe and impurities. Welding heat input is about 2.0 to 3-.0kJ/cm. In order to prevent a surface of the two-phase stainless steel from being oxidized and to improve welding quality thereof, mixing gas including inert gas, such as argon gas, and nitrogen gas is provided from a welding torch. At this time, 2-20% of nitrogen gas is added to argon gas. Nitrogen gas is supplied as backing gas in such a manner that an austenite-phase and a ferrite-phase are uniformly formed.
展开▼