METHOD FOR PRODUCING ALLOY LAMINATE MATERIAL CONTAINING DISPERSED QUASICRYSTAL GRAINS, METHOD FOR PRODUCING ALLOY BULK MATERIAL CONTAINING DISPERSED QUASICRYSTAL GRAINS, ALLOY LAMINATE MATERIAL CONTAINING DISPERSED QUASICRYSTAL GRAINS, AND ALLOY BULK MATERIAL CONTAINING DISPERSED QUASICRYSTAL GRAINS
METHOD FOR PRODUCING ALLOY LAMINATE MATERIAL CONTAINING DISPERSED QUASICRYSTAL GRAINS, METHOD FOR PRODUCING ALLOY BULK MATERIAL CONTAINING DISPERSED QUASICRYSTAL GRAINS, ALLOY LAMINATE MATERIAL CONTAINING DISPERSED QUASICRYSTAL GRAINS, AND ALLOY BULK MATERIAL CONTAINING DISPERSED QUASICRYSTAL GRAINS
PROBLEM TO BE SOLVED: To provide a method for producing an alloy laminate material containing dispersed quasicrystal grains which can be made into a thick plate or a member for structures having a specified shape, particularly having a complicated shape as containing quasicrystal grains, and whose strength when being used as a member for structures, particularly strength in a high temperature environment can be increased.;SOLUTION: The method for producing an alloy laminate material containing dispersed quasicrystal grains 1 is characterized in that alloys containing dispersed quasicrystal grains each obtained by dispersing quasicrystal grains into a matrix are laminated on a base material 2 at the decomposition temperature of the quasicrystal grains or below by a laminating apparatus 100, so as to produce the alloy laminate material containing dispersed quasicrystal grains 1.;COPYRIGHT: (C)2009,JPO&INPIT
展开▼