Production manner, and high tenacious tool null of high tenacious

机译：生产方式和高韧性工具高韧性的无效

页面导航

摘要
著录项
相似文献

摘要

PROBLEM TO BE SOLVED: To provide a method for efficiently manufacturing a tool with high toughness, which has crystal grains refined and prevents the destruction during use.;SOLUTION: This manufacturing method employs a steel material containing 0.40-0.85% C (mass%, hereafter), 2.0% or less Si (not including 0%), 2.0% or less Mn (not including 0%), 3.0% or less Cr (not including 0%), 0.1% or less Al (not including 0%), and 0.007 to 0.015% N, and subjects it to thermal refining treatment, wherein the thermal refining treatment comprises the steps of heating it to a temperature in an austenitic range, then cooling it to an A_r3 transformation temperature to (A_r3 transformation temperature + 50°C), and quenching it from the temperature range.;COPYRIGHT: (C)2004,JPO&NCIPI

机译：解决的问题：提供一种有效地制造具有高韧性的工具的方法，该工具具有细化的晶粒并防止使用过程中的破坏。;解决方案：此制造方法使用的碳钢含量为0.40-0.85％（质量％，以下），Si≤2.0％（不包括0％），Mn≤2.0％（不包括0％），Cr≤3.0％（不包括0％），Al≤0.1％（不包括0％）和0.007至0.015％的N，然后对其进行热精处理，其中热精处理包括以下步骤：将其加热到奥氏体温度，然后冷却至A _{r3 相变到（A r3 转变温度+ 50°C），然后在该温度范围内淬灭。;版权所有：（C）2004，日本特许厅}

著录项

公开/公告号JP3908661B2

专利类型
公开/公告日2007-04-25

原文格式PDF
申请/专利权人株式会社神戸製鋼所;
展开▼

申请/专利号JP20020376011
发明设计人藏本廣志;茨木信彦;
展开▼

申请日2002-12-26
分类号C21D9/00;B25B13/00;B25B15/00;C22C38/00;C22C38/38;C22C38/58;