MANUFACTURING METHOD OF WIDE AND THICK PLATE HAVING EXCELLENT STRENGTH AND TOUGHNESS FOR MAKING LINEPIPE
MANUFACTURING METHOD OF WIDE AND THICK PLATE HAVING EXCELLENT STRENGTH AND TOUGHNESS FOR MAKING LINEPIPE
展开▼
机译:具有出色的强度和韧性的生产线管的宽厚板的制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
line pipe of the present invention is used steel pipes for use in steel manufacturing method for a wide humul about that, more particularly, to low plate deformation after manufacture can be reduced while the constraints on the equipment on the production process to increase the size of the steel sheet can be produced. ; the method for manufacturing the steel sheet of the present invention the wide humul is, C: 0.04 ~ 0.1%, Si: 0.1 ~ 0.4%, Mn: 1.3 ~ 1.8%, Sol. Al: 0.01 ~ 0.05%, Ti: 0.005 ~ 0.02%, Nb: 0.02 ~ 0.06%, V: less than 0.1%, Mo: less than 0.1%, P: less than 0.02%, S: not more than 0.005%, balance Fe and other unavoidable heating in the range of 1050 ~ 1150 by targeting a steel slab consisting of impurity contained in; Reduction ratio of austenite at a temperature below the recrystallization temperature knight 70-80% in the finish rolling step of producing the steel sheet; Step of cooling the steel sheet in the range of the cooling rate 5 ~ 8 / sec; And to step 450 to cooling stop at a temperature of 550 ;. Comprises a
展开▼