首页> 外国专利> Co-Ni-Al Shape memory alloy and method for producing same

Co-Ni-Al Shape memory alloy and method for producing same

机译：Co-Ni-Al形状记忆合金及其制造方法

页面导航

摘要
著录项
相似文献

摘要

A shape memory alloy comprises Co, Ni and Al with a two-phase structure comprising a β-phase having a B2 structure and a γ-phase having an fcc structure, at least 40% by area of crystal grain boundaries of the β-phase being occupied by the γ-phase. The shape memory alloy can be produced by a first heat treatment step comprising heating at 1200 to 1350°C for 0.1 to 50 hours and cooling at 0.1 to 1000°C/minute, and a second heat treatment step comprising heating at 1000 to 1320°C for 0.1 to 50 hours and cooling at 10 to 10000°C/minute.

机译：形状记忆合金由Co，Ni和Al构成，该Co，Ni和Al为两相结构，该两相结构的B晶相的面积至少为40％，该B相具有B2结构的β相和具有fcc结构的γ相。被γ相占据。形状记忆合金可通过包括在1200至1350℃下加热0.1至50小时并以0.1至1000℃/分钟冷却的第一热处理步骤以及包括在1000至1320℃下加热的第二热处理步骤来生产。保持0.1至50小时，并以10至10000℃/分钟冷却。

著录项

公开/公告号EP1460139B1

专利类型
公开/公告日2006-05-31

原文格式PDF
申请/专利权人 HONDA MOTOR CO LTD;ISHIDA KIYOHITO;NAT INST OF ADVANCED IND SCIEN;
展开▼

申请/专利号EP20040251559
发明设计人 OHTA MASAHIROKK HONDA GIJUTSU KENKYUJO;OIKAWA KATSUNARI;TANAKA YUUKI;SUKIGARA TORUKK HONDA GIJUTSU KENKYUJO;ISHIDA KIYOHITO;KAINUMA RYOSUKE;
展开▼

申请日2004-03-18
分类号C22C19/00;C22C19/07;C22F1/10;
国家 EP
入库时间 2022-08-21 21:30:16

相似文献

专利
外文文献
中文文献