PROBLEM TO BE SOLVED: To obtain stockings excellent in transparency and durability or the like. ;SOLUTION: This covered elastic yarn obtained by coiling a polyamide filament as a covering yarn around an elastic yarn as a core yarn comprises the polyamide filament having 5-15 de yarn size, 1-15 filament count, ≥8.0 g/de strength and ≤40% elongation. The stockings are obtained by using the covered elastic yarn at least at one part of leg parts. The production method of the covering yarn for the covered elastic yarn is characterized by spinning a polyamide having ≤2.9 relative viscosity at ≥3,000 m/min spinning speed, drawing and heat-treating the spun yarn without winding the yarn to provide the polyamide filament having 40×10-3-50×10-3 birefringence and 1.130-1.135 g/cm3 density, and subjecting the obtained polyamide filament to heat-drawing of ≥1.05 times.;COPYRIGHT: (C)1999,JPO
展开▼
机译:要解决的问题:获得透明性和耐久性等优异的长袜。 ;解决方案:通过将聚酰胺长丝作为包覆丝卷绕在作为芯线的弹性丝周围而获得的这种包覆弹性丝包括具有5-15 de纱线尺寸,1-15长丝支数,≥8.0g / de强度和伸长率≤40%。通过在腿部的至少一部分处使用包覆的弹性纱来获得长筒袜。包覆弹性纱的包覆纱的制造方法,其特征在于,以≥3,000m/ min的纺丝速度对相对粘度≤2.9的聚酰胺进行纺丝,不卷绕而进行纺丝并进行牵伸热处理,从而得到具有40×10 -3 Sup> -50×10 -3 Sup>双折射和1.130-1.135 g / cm 3 Sup>密度,并将获得的聚酰胺长丝进行吸热≥1.05倍;版权所有:(C)1999,日本特许厅
展开▼