Cobalt winning by selective redn. of slag with iron - where molten slag is mixed with solid or molten iron to obtain ferrous alloy contg. cobalt and copper
Cobalt winning by selective redn. of slag with iron - where molten slag is mixed with solid or molten iron to obtain ferrous alloy contg. cobalt and copper
展开▼
机译:通过选择性重做获得钴。渣与铁的混合-将熔融渣与固态或熔融铁混合以获得含铁合金。钴和铜
展开▼
页面导航
摘要
著录项
相似文献
摘要
The slag contains 0.5-3% Co as oxide, 30% max. iron oxide, and small amts. of Ni and Cu; and the molten slag is mixed with a fine reducing agent contg. min. 80% and pref. min. 90% iron. The pref. reducing agents are molten iron contg. max. 4.5% C and max. 3% Si; or solid iron crushed to size 0.5 mm; or crushed solid iron formed into an agglomerate with the slag and heated at 700-1000 degrees C to reduce all the Co oxide, Fe, and possibly Ni and Cu. Molten slag may alternately be fed in counter-current to molten iron in a two stage process for winning Co. Used for winning Co from slags with low Co content and obtd. during the treatment of Co ores which may contain Cu.
展开▼