Produced by powder metallurgy by sintering, precipitation, corrosion - and high temperature-resistant nickel chromium - alloy
Produced by powder metallurgy by sintering, precipitation, corrosion - and high temperature-resistant nickel chromium - alloy
展开▼
机译：通过粉末冶金通过烧结，沉淀，腐蚀和耐高温镍铬合金生产
展开▼
页面导航
摘要
著录项
相似文献
摘要
An age hardenable, corrosion and heat resistant nickel-chromium, refractory carbide alloy is provided by powder metallurgy for use at elevated temperatures as high as 2000 DEG F (1090 DEG C) comprising primary grains of at least one refractory carbide selected from the group consisting of TiC, CbC, VC and TaC dispersed through a matrix of an age hardenable, corrosion and heat resistant nickel-chromium alloy consisting essentially by weight of about 5 to 30 percent chromium, up to about 15 percent iron, about 0.5 to 5 percent titanium, about 0.2 to 5 percent aluminum, up to about 25 percent cobalt, up to about 0.25 percent carbon and the balance essentially nickel.