首页> 外国专利> Abrasion-resistant steel plate and method of producing abrasion-resistant steel plate

Abrasion-resistant steel plate and method of producing abrasion-resistant steel plate

机译：耐磨钢板及生产耐磨钢板的方法

页面导航

摘要
著录项
相似文献

摘要

An abrasion-resistant steel plate comprises: a specific chemical composition; and a microstructure in which a volume fraction of martensite at a depth of 1 mm from a surface of the abrasion-resistant steel plate is 90% or more, and a prior austenite grain size in a plate thickness central part at the mid-thickness of the abrasion-resistant steel plate is 80 μm or less, wherein hardness at a depth of 1 mm from the surface of the abrasion-resistant steel plate is 460 to 590 HBW 10/3000 in Brinell hardness, and a concentration [Mn] of Mn in mass % and a concentration [P] of P in mass % in a plate thickness central segregation area satisfy 0.04[Mn]+[P]<0.50.

机译：耐磨钢板包括：特定的化学成分; 和一个微观结构，其中来自耐磨钢板的表面的1mm深度的马氏体的体积分数为90％或更高，并且在板厚中央部件中的先前奥氏体晶粒尺寸耐磨钢板为80μm或更小，其中距离耐磨钢板表面的深度为1mm的硬度为360至590hbw 10/3000在Brinell硬度，以及Mn的浓度[Mn] 在板厚中央隔离面积中质量％和P质量％的浓度[p]质量％满足0.04 [Mn] + [p] <0.50。

著录项

公开/公告号US11111556B2

专利类型
公开/公告日2021-09-07

原文格式PDF
申请/专利权人 JFE STEEL CORPORATION;
展开▼

申请/专利号US201616092553
发明设计人 YUSUKE TERAZAWA;NAOKI TAKAYAMA;KENJI HAYASHI;KAZUKUNI HASE;
展开▼

申请日2016-04-19
分类号C21D8/02;C22C38;C22C38/02;C22C38/04;C22C38/06;C22C38/20;C22C38/22;C22C38/24;C22C38/26;C22C38/50;C22C38/54;C22C38/18;C22C38/40;B22D11/12;C22C38/38;C22C38/32;C22C38/28;B22D11;C21D9/46;C22C38/58;B22D11/041;C21D6;C22C38/44;
国家 US
入库时间 2022-08-24 20:52:42