This paper reports the utilization of high ionic strength (>1100 mM) calcium phosphate solutions in depositing 20-65 nm-thick, bonelike apatitic calcium phosphate on Ti6A14V within 2 to 6 hours, at room temperature. The solution used here multiplied the concentrations of calcium and phosphate ions in human plasma or synthetic/simulated body fluid (SBF) by a factor of ten. The solutions did not contain any buffering agents, such as Tris or Hepes. With these solutions there was no CO_2 bubbling required. The carbonate content (8 wt%) and Ca/P molar ratio (1.57) of the coated calcium phosphates qualified them as bonelike. The same solutions were successfully used in coating macroporous p-TCP (p-tricalcium phosphate, β-Ca_3(PO_4)_2) cylinders and macroporous collagen membranes with apatitic calcium phosphate.
机译：本文报道了在室温下2至6小时内，高离子强度（> 1100 mM）磷酸钙溶液在Ti6A14V上沉积20-65 nm厚的骨状磷灰石磷酸钙的应用。此处使用的溶液将人体血浆或合成/模拟体液（SBF）中钙和磷酸根离子的浓度乘以十倍。该溶液不包含任何缓冲剂，例如Tris或Hepes。使用这些解决方案，无需冒泡的CO_2。涂覆的磷酸钙的碳酸盐含量（8wt％）和Ca / P摩尔比（1.57）使它们成为骨状。相同的解决方案已成功用于用apaptic磷酸钙涂覆大孔p-TCP（p-磷酸三钙，β-Ca_3（PO_4）_2）圆柱体和大孔胶原膜。