Development of high heat resistant transparent or white crystalline mold products with high melt viscosity PET from recovered PET bottles

机译：高耐热透明或白色晶体模具产品，具有高熔体粘度宠物的高熔透明或白色晶体模具产品来自回收的PET瓶子

获取原文

页面导航

摘要
著录项
相似文献
相关主题

摘要

HMV PET(polyethylene terephthalate with high melt viscosity and high molecular weight) was produced by the reactive processing method from recovered PET bottle flakes, a small amount of epoxide as coupling agent and catalysts at 270～280°C, and directly processed into sheets and boards. Clear sheets of 0.4 mm thickness were made with designated T/D ratio of 25/75 and 50/50, which T and D meaned di- and tri-glycidyl ether of epoxides respectively, showed high recrystallization rates over 5～10 times at 150～180°C for commercial A-PET sheet with linear molecular structure. Clear boards of 2 mm thickness and designated T/D ratio 50/50 were molded by the thermoforming under vacuum and pressure into clear crystalline cups with heat resistant temperature of 80～100°C and white crystalline cup with heat resistant temperature of about 200°C.

机译：通过回收的PET瓶薄片，作为偶联剂和270〜280℃的偶联剂和催化剂，通过反应加工方法制备HMV PET（具有高熔体粘度和高分子量的聚对苯二甲酸乙烯和高分子量）。在270〜280℃下催化剂，并直接加工成片材和催化剂董事会。用指定的T / D比为25/75和50/50的透明片材，分别为25/75和50/50的25/75和50/50，分别为环氧化物的T和D表示的二甘油醚，在150时显示出高出5〜10次的高分结晶率用于具有线性分子结构的商业A-PET板〜180°C。透明板2毫米厚度和指定的T / D比50/50通过热成型在真空和压力下进行成型，进入透明的结晶杯，耐热温度为80〜100°C和白色晶杯，耐热温度约为200° C。

著录项

来源
《プラスチック成形加工学会年次大会》|2004年||共2页
会议地点
作者
Takashi FUJIMAKI;
展开▼
作者单位

展开▼
会议组织
原文格式 PDF
正文语种
中图分类 TG3-53;
关键词
PET with high melt viscosity; Reactive processing method; High recrystallization rates of PET; High heat resistant molded PET;

机译：具有高熔体粘度的宠物;反应加工方法;宠物高再结合率;高耐热成型宠物;

相似文献

外文文献
中文文献
专利

1. Conversion from Hot Filling System for Blown Heat Resistant Bottles to Inline High-speed Aseptic Filling System for Preformed Blown PET Bottles [J] . N.Kawanami 包装技術 . 2001,第9期

机译：从吹制耐热瓶的热灌装系统转换为预制吹制PET瓶的在线高速无菌灌装系统
2. Conversion from Hot Filling System for Blown Heat Resistant Bottles to Inline High-speed Aseptic Filling System for Preformed Blown PET Bottles [J] . N.Kawanami 包装技術 . 2001,第9期

机译：从耐热吹塑瓶的热灌装系统转换为预制吹塑PET瓶的在线高速无菌灌装系统
3. KINETICS AND THERMAL CRYSTALLINITY OF RECYCLED PET .2. TOPOGRAPHIC STUDY ON THERMAL CRYSTALLINITY OF THE INJECTION-MOLDED RECYCLED PET [J] . Fann DM., Huang SK., Lee JY. Journal of Applied Polymer Science . 1996,第2期

机译：再生PET的动力学和热结晶性.2。注射成型回收PET热结晶度的拓扑学研究
4. Development of high heat resistant transparent or white crystalline mold products with high melt viscosity PET from recovered PET bottles [C] . Takashi FUJIMAKI プラスチック成形加工学会年次大会 . 2004

机译：高耐热透明或白色晶体模具产品，具有高熔体粘度宠物的高熔透明或白色晶体模具产品来自回收的PET瓶子
5. A history of the H. N. White Company and its products (1893--1965) including a comparison of White's cornet and trumpet models with those in the collections of the National Music Museum. [D] . Spell, Clinton E. 2013

机译：H. N. White Company及其产品的历史（1893--1965年），包括将White的短号和小号模型与国家音乐博物馆收藏的模型进行比较。
6. Effects of Heating and Cooling of Injection Mold Cavity Surface and Melt Flow Control on Properties of Carbon Fiber Reinforced Semi-Aromatic Polyamide Molded Products [O] . Yasuhiko Murata, Ryota Kanno 2021

机译：注塑模腔表面加热和冷却的影响及熔体流动控制对碳纤维增强半芳族聚酰胺模塑产品的性能
7. Development of Molding Materials and Molded Parts from Recycled PET Bottles. [O] . Takeshi Moriwaki, Toshiharu Sakaguchi, Izumi Yamazaki, 1998

机译：从再生的PET瓶子开发成型材料和模塑部件。

Development of high heat resistant transparent or white crystalline mold products with high melt viscosity PET from recovered PET bottles

摘要

著录项

相似文献

相关主题

期刊订阅