首页> 外文会议>International Conference on Advanced Engineering Materials and Technology >Fabrication and Properties of Corn Husk Fiber / Polylactic Acid Fiberboard
【24h】

Fabrication and Properties of Corn Husk Fiber / Polylactic Acid Fiberboard

机译：玉米壳纤维/聚乳酸纤维板的制造与性能

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this study corn husk used as raw material, and achieved corn husk fiber through degumming properly. Then degradable fiberboard can be obtained with husk fiber and polylactic acid particles through blending and hot pressing. Taking mass fraction and length of corn husk fiber, hot-pressing time and temperature as factors, and taking tensile, bending and impact strength as index, through the L9 (34) orthogonal testing and range analyzing and achieved the optimal process parameters is: corn husk fiber mass fraction is 50%, corn husk fiber length is 10 mm, hot pressing time is 6 min, hot pressing temperature is 180°C. Under the optimal process condition, a optimal fiberboard is obtained, whose tensile strength is 69.32 MPa, bending strength is 90.26 MPa, impact strength is 18.5 KJ/m2. The conclusion of this paper provides the theoretical guidance for the reuse technology of corn husk fiber.
机译：在这项研究中，玉米壳用作原料，并通过正确脱胶实现玉米壳纤维。然后可以通过混合和热压用壳纤维和聚乳酸颗粒获得可降解的纤维板。玉米壳纤维的质量分数和长度，热压时间和温度为因素，以及通过L9（34）正交检测和范围分析并达到最佳工艺参数的抗拉，弯曲和冲击强度作为指数的抗拉，弯曲和冲击强度。玉米壳纤维质量分数为50％，玉米壳纤维长度为10毫米，热压时间为6分钟，热压温度为180℃。在最佳过程条件下，获得最佳纤维板，其拉伸强度为69.32MPa，弯曲强度为90.26MPa，冲击强度为18.5 kJ / m 2。本文的结论为玉米壳纤维的重用技术提供了理论指导。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号