首页> 外文会议>IUMRS International Conference in Asia >Low temperature growth of ZnO nanorod on various substrates by solution chemical method
【24h】

Low temperature growth of ZnO nanorod on various substrates by solution chemical method

机译：通过溶液化学方法对各种基材上的ZnO纳米棒的低温生长

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The ZnO seed precursor was prepared by sol-gel reaction. ZnO nanorod arrays were fabricated by solution chemical deposition on ZnO coated seed substrates. The substrates used are Si wafer, glass and PET. The fabricated ZnO nanorod had hexagonal morphology, length of 400～500 nm and diameter of 25～50 nm. The ZnO seeds were indispensable for the aligned growth of ZnO nanorod. The ZnO nanorod growth was dependent on the seeding method used but independent of the substrates. The structure of ZnO nanorod was characterized by FE-SEM, XRD and FE-TEM. This method enables large scale growth of ZnO arrays on all kinds of substrates including polymers.
机译：通过溶胶 - 凝胶反应制备ZnO种子前体。通过ZnO涂层种子基材上的溶液化学沉积来制造ZnO纳米棒阵列。使用的基板是Si晶片，玻璃和宠物。制造的ZnO纳米棒具有六边形形态，长度为400〜500nm，直径为25〜50nm。 ZnO种子对于ZnO纳米棒的对齐生长是必不可少的。 ZnO纳米棒的生长取决于所用但独立于基材的播种方法。通过Fe-SEM，XRD和FE-TEM的特征在于ZnO纳米棒的结构。该方法使得ZnO阵列的大规模增长在包括聚合物的各种基板上。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号