首页> 外文会议>International Conference on Aluminum Alloys >HRTEM OBSERVATION OF THE PRECIPITATES IN Cu AND Ag ADDED Al-Mg-Si ALLOYS
【24h】

HRTEM OBSERVATION OF THE PRECIPITATES IN Cu AND Ag ADDED Al-Mg-Si ALLOYS

机译：HRTEM观察Cu和Ag中的沉淀物加入Al-Mg-Si合金

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this study, the aging behaviour of Al-1.0mass%Mg_2Si alloys containing 0.35at.%Cu, 0.35at.%Ag, 0.2at.%Cu-0.1at.%Ag and 0.1at.%Cu-0.2at.%Ag has been investigated by hardness measurement and HRTEM observation. 0.35Cu alloy has the highest peak hardness. 0.1Cu-0.2Ag alloy has the shortest aging time to the peak hardness. 0.1Cu-0.2Ag alloy has the fastest age-hardening rate in the early period of aging. 0.35Ag alloy has the finest microstructure at the peak hardness. The precipitates were classified into random-type, parallelogram-Q'-phase using HRTEM image with different aging time. Relative frequency of all types of precipitates changed by aging times.
机译：在该研究中，Al-1.0mass％Mg_2SI合金的老化行为含有0.35At。％Cu，0.35At％Ag，0.2At。％Cu-0.1At。％Ag和0.1At。％Cu-0.2At。％ 通过硬度测量和HRTEM观察研究了AG。 0.35cu合金具有最高的硬度。 0.1CU-0.2AG合金具有最短的峰值硬度的老化时间。 0.1Cu-0.2Ag合金在衰老时期具有最快的硬化率。 0.35Ag合金在峰值硬度处具有最佳的微观结构。 使用具有不同老化时间的HRTEM图像将沉淀物分为随机型，平行四边形-Q'-阶段。 所有类型的沉淀物的相对频率通过老化时间改变。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号