首页> 外文会议>International Conference on Chemical, Material and Metallurgical Engineering >Recovery of iron from cyanide tailings with reduction roasting-water leaching- magnetic separation
【24h】

Recovery of iron from cyanide tailings with reduction roasting-water leaching- magnetic separation

机译：从氰化物尾矿恢复铁，减少焙烧 - 水浸出 - 磁性分离

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Cyanide tailings have become one kind of the most hazardous solid waste. In order to recycle iron in the cyanide tailings, we present a technique using roasting- water leaching- magnetic separation. After analysis of the different parameters on recovery efficiency of iron, the optimum reaction parameters were proposed as the following: in reduction roasting process, weight ratios of cyanide tailings/activated carbon at 100:10, roasting at 750°C; the liquid to solid ratio is 15:1 (ml/g), leaching at 60°C for 5 min at water leaching. The grade of magnetic concentrate 53.8231%Fe and recovery rate of 76.5458% were obtained. Mineralography of roasted product, water-leached sample were studied by X-ray powder diffraction technique (XRD).
机译：氰化物尾矿已成为一种最危险的固体废物。为了在氰化物尾矿中循环铁，我们使用焙烧 - 水浸出磁性分离的技术。在分析钢铁恢复效率的不同参数之后，提出了最佳反应参数如下：在减少烘焙过程中，氰化物尾矿/活性炭的重量比在100：10，在750℃下焙烧;液体至固体比为15：1（mL / g），在水浸出时在60℃下浸出5分钟。获得磁性浓缩物的等级53.8231％Fe和回收率为76.5458％。通过X射线粉末衍射技术（XRD）研究了焙烧产品的矿物浸出样品。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号