Mesoporous hydroxylapatite was prepared by Liquid phase precipitation method, using Polystyrene microspheres as template. Polystyrene microspheres mixed uniformly with the prepared hydroxylapatite slurry, then the mixture dryed and sintered at reasonable temperature, mesoporous hydroxylpatite ceramics were obtained. The phase constituent was analyzed by X-ray diffraction(XRD) and the microstructure was observed under scanning electron microscopy (SEM). The results showed that the prepared mesoporous hydroxylapatite ceramics were of high purity and their pores were evenly distributed, with big pore 0.8-1.0 um and small pore 30-80nm in diameter.
机译：通过液相沉淀法制料，使用聚苯乙烯微球作为模板制备介孔羟基磷灰石。聚苯乙烯微球与制备的羟基磷灰石浆料均匀混合，然后在合理的温度下干燥和烧结的混合物，获得介孔的羟晶岩陶瓷。通过X射线衍射（XRD）分析相成分，并且在扫描电子显微镜（SEM）下观察到微观结构。结果表明，制备的介孔羟基磷灰石陶瓷具有高纯度，其孔隙均匀分布，大孔0.8-1.0μm和直径小孔30-80nm。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号