首页> 外文会议>International Conference on Modern Building Materials, Structures, and Techniques >Relaxation modulus of SMA with polymer modified and highly polymer modified bitumen
【24h】

Relaxation modulus of SMA with polymer modified and highly polymer modified bitumen

机译：SMA与聚合物改性和高度高聚合物改性沥青的放松模量

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The article presents the test results of the relaxation modulus of SMA. The samples of SMA mixture were made using polymer modified bitumen PMB 45 / 80-55 (PMB-N) and highly polymer modified bitumen PMB 45 / 80-80 (PMB-HM). Determination of the relaxation modulus were made using DT-CY test (direct tensile test) at 10°C, 20°C and 40°C. To describe the relaxation phenomenon of the bituminous mixture a logit model has been used. The test results indicates that the use of the highly modified bitumen (PMB-HM) caused the increase in the stiffness modulus SMA at high temperature / low frequencies. As a result, the presence of highly polymer modified bitumen will increase the resistance to the permanent deformation of SMA.
机译：该物品介绍了SMA的松弛模量的测试结果。使用聚合物改性沥青PMB 45 / 80-55（PMB-N）和高分子改性沥青PMB 45 / 80-80（PMB-HM）制备SMA混合物的样品。使用DT-Cy测试（直接拉伸试验）在10℃，20℃和40℃下进行弛豫模量的测定。为了描述沥青混合物的弛豫现象已经使用了Logit模型。测试结果表明，使用高度改性的沥青（PMB-HM）导致高温/低频下刚度模量SMA的增加。结果，高分子改性沥青的存在将增加对SMA的永久变形的抵抗力。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号