Dynamic delamination experiments were performed on the specimens made of unidirectional glass fiber composites in Mode I and Mode II. Crack propagation history was analyzed using a high speed camera synchronized with electrical circuit device. The results showed that the dynamic fracture toughness was increased with increasing loading rate in Mode I and Mode II fracture experiments. The loading rate and surface topography effects on energy dissipation during dynamic fracture of an aluminum/epoxy interface were also experimentally investigated. The results indicated that surface morphology significantly affect the energy dissipation during the dynamic fracture of the interface.
机译：在模式I和模式II下，对由单向玻璃纤维复合材料制成的样品进行了动态分层实验。使用与电路装置同步的高速摄像机分析了裂纹的传播历史。结果表明，在模式I和模式II断裂实验中，动态断裂韧性随加载速率的增加而增加。还通过实验研究了加载速率和表面形貌对铝/环氧树脂界面动态断裂过程中能量耗散的影响。结果表明，表面形貌显着影响界面动态断裂过程中的能量耗散。

著录项

  • 作者

    Syn, Chul Jin.;

  • 作者单位

    Purdue University.;

  • 授予单位 Purdue University.;
  • 学科 Engineering Aerospace.
  • 学位 Ph.D.
  • 年度 2008
  • 页码 127 p.
  • 总页数 127
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 航空、航天技术的研究与探索;
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号