Characterizations of precipitation behavior of Al-Mg-Si alloys under different heat treatments

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The solidification-precipitation behavior of Al-Mg-Si multicomponent alloys has long been an absorbing topic. Experiments were carried out to analyze the precipitation behaviors of Al-Mg-Si alloys under different heat treatments. All specimens were homogenized at 570 °C for 8 h, and then solution treated at 540 °C for 55 min. Subsequently, the specimens were age treated for different times at temperatures of 100 °C, 150 °C and 180 °C, respectively. The experimental results show that the occurrence of dispersed free zones(DFZ) is caused by the uneven distribution of dispersed phase. During the aging process, pre-β″ phases form at the initial stage and an aging temperature of 100 °C is too low to complete the transformation of pre-β″ to β″. At 150 °C, the precipitation sequence is concluded as SSSS-pre-β″-pre-β″+β″-β″-β′-β. Moreover, changes in sizes and densities of the pre-β″, β″and β′ phases during the aging process has an important influence on the evolution of microhardness and electrical resistivity. The microhardness peak value of 150 °C is similar to that of 180 °C, which is ~141 HV. While, at 100 °C, the microhardness increases slowly, and the attainable value is 127 HV up to 19 days. When the aging temperature is 100 °C, the electrical resistivity has the highest average value. When the aging temperature exceeds 100 °C, with the occurrence and growth of β″and β′, the resistivity has a distinct decrease with prolonged aging time.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号