首页> 中文期刊> 《中国铸造：英文版》 >Study on in-situ WC particles/tungsten wire reinforced iron matrix composites under electromagnetic field

Study on in-situ WC particles/tungsten wire reinforced iron matrix composites under electromagnetic field

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

By applying electromagnetic field to a system consisting of tungsten wires and grey cast iron melt,the grey cast iron matrix composite reinforced by either in-situ WC particles or the combination ofin-situ WC particles and the residual tungsten wire was obtained.By means of differential thermal analysis(DTA),the pouring temperature ofiron melt was determined at 1,573 K.The microstructures of the composites were analyzed by using of X-ray diffraction(XRD),scanning electron microscopy(SEM) equipped with an energy dispersive spectrum(EDS) and pin-on-disc abrasive wear test.The obtained results indicated that,with the enhancing frequency of electromagnetic field,the amount ofin-situ WC particles gradually increases,leading to continuous decrease of the residual tungsten wires.When the electromagnetic field frequency was up to 4 kHz,tungsten wires reacted completely with carbon atoms in grey cast iron melt,forming WC particals.The electromagnetic field appeared to accelerate the elemental diffusion in the melt,to help relatively quick formation of a series of small FeW-C ternary zones and to improve the kinetic condition ofin-situ WC fabrication.As compared with the composite prepared without the electromagnetic field,the composite fabricated at 4 kHz presented good wear resistance.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号