首页> 中文期刊> 《中国铸造：英文版》 >Segregation in squeeze casting 6061 aluminum alloy wheel spokes and its formation mechanism

Segregation in squeeze casting 6061 aluminum alloy wheel spokes and its formation mechanism

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Segregation can seriously damage the mechanical properties of the aluminum alloys.6061 aluminum alloy wheel spokes were prepared by squeeze casting.To investigate the formation mechanism of segregation,the microstructure of the alloy was observed using scanning electron microscopy,energy dispersive spectrometry,X-ray diffraction and electron microprobe analysis methods.The Gibbs energy of each phase during solidification was calculated by JMat Pro.Results show that the segregation phases in the R-joint of the wheel spokes are mainly composed of Mg_(2)Si,β-Al Fe Si and Al_(5)Cu_(2)Mg_(8)Si_(6)intermetallics.During the solidification of the 6061 aluminum alloy wheels,Mg_(2)Si andα-Al Fe Si phases precipitate in the mushy zone at first.With the decrease of temperature,α-Al Fe Si transforms intoβ-Al Fe Si,while Al_(5)Cu_(2)Mg_(8)Si_(6)precipitates from the solid-state aluminum alloy after solidification.Segregation at the R-joint of wheel spokes is mainly caused by insufficient cooling,so the cooling during alloy solidification should be enhanced to avoid segregation.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号